2024 Aluminum Alloy
AMS 4037, AMS 4120, AMS 4192, AMS 7223
UNS A92024
Please call 800-707-6061 or fax RFQs to
800-707-3439. We will get back to you ASAP. Thanks.
* All Trademarks and/or Trade
names are the properties of their respective owners.
Aluminum 2024 Data Sheet
(view complete data sheet for this material - including material property
data, metal compositions, etc)
California Metal & Supply is a leading supplier of
quality
2024 Aluminum Sheet, 2024 Aluminum Plate, 2024 Aluminum Bar.
Aluminum 2024 alloy has good machinability and good
mechanical properties. As a light alloy, Aluminum 2024 is an ideal design choice for a
multitude of applications.
Aluminum 2024 Applications: Aluminum 2024 is typically
used in aircraft structures, rivets, connectors, hydraulic valve bodies and
miscellaneous structural applications.
Aluminum 2024 Specifications: UNS A92024, Aluminum 2024, 2024
Alloy, 2024 Aluminum Alloy, AA2024
Aluminum 2024 Available Forms: 2024
Aluminum Sheet, 2024 Aluminum Plate, 2024 Aluminum Bar
2024 Aluminum Sheet, 2024 Aluminum Plate
Temper: 2024-0, 2024-T3,
2024-T81,
2024-T351, 2024-T851
Bare: QQ-A-250/4, AMS
4035, AMS 4037, FMS 10101
Clad: QQ-A-250/5, AMS
4040, AMS 4041, BMS 7-305
2024-0 Bare Aluminum
Sheet Per AMS-QQ-A-250/4
2024-0 Alclad Aluminum
Sheet Per AMS 4035, AMS-QQ-A-250/5
2024-T3 Bare Aluminum
Sheet Per AMS-QQ-A-250/4
2024-T3 Alclad Aluminum
Sheet Per AMS-QQ-A250/5
2024-T3 Alclad MRS
Quality Aluminum Sheet Per QQ-A-250/5
2024-T351 Aluminum
Plate per AMS-QQ-A250/4
Mill: Alcoa, Kaiser, Alcan
We are a certified
distributor of Aluminum 2024 alloy in sheets, plates, bars, and tubing in
various specifications.
2024
Aluminum Bar (Cold Finish and Extruded)
2024 Aluminum Material Properties
Physical Properties
| |
Metric |
English |
Comments |
| |
|
Density |
2.78 g/cc |
0.1 lb/in³ |
AA; Typical |
Mechanical Properties |
| |
|
Hardness, Brinell |
47 |
47 |
AA; Typical; 500
g load; 10 mm ball |
|
Ultimate Tensile Strength |
186 MPa |
27000 psi |
AA; Typical |
|
Tensile Yield Strength |
75.8 MPa |
11000 psi |
AA; Typical |
|
Elongation at Break |
20 % |
20 % |
AA; Typical;
1/16 in. (1.6 mm) Thickness |
|
Elongation at Break |
22 % |
22 % |
AA; Typical; 1/2
in. (12.7 mm) Diameter |
|
Modulus of Elasticity |
73.1 GPa |
10600 ksi |
AA; Typical;
Average of tension and compression. Compression modulus is about 2%
greater than tensile modulus. |
|
Ultimate Bearing Strength |
345 MPa |
50000 psi |
Edge
distance/pin diameter = 2.0 |
|
Bearing Yield Strength |
131 MPa |
19000 psi |
Edge
distance/pin diameter = 2.0 |
|
Poisson's Ratio |
0.33 |
0.33 |
|
|
Fatigue Strength |
89.6 MPa |
13000 psi |
AA; 500,000,000
cycles completely reversed stress; RR Moore machine/specimen |
|
Machinability |
30 % |
30 % |
0-100 Scale of
Aluminum Alloys |
|
Shear Modulus |
28 GPa |
4060 ksi |
|
|
Shear Strength |
124 MPa |
18000 psi |
AA; Typical |
Electrical Properties |
| |
|
Electrical Resistivity |
3.49e-006 ohm-cm |
3.49e-006 ohm-cm |
AA; Typical at
68 Degrees F |
Thermal Properties |
| |
|
CTE, linear 68 Degrees F |
23.2 µm/m- Degrees C |
12.9 µin/in- Degrees F |
AA; Typical;
Average over 68-212 Degrees F range. |
|
CTE, linear 250 Degrees C |
24.7 µm/m- Degrees C |
13.7 µin/in- Degrees F |
Average over the
range 20-300 Degrees C |
|
Heat Capacity |
0.875 J/g- Degrees C |
0.209 BTU/lb- Degrees F |
|
|
Thermal Conductivity |
193 W/m-K |
1340 BTU-in/hr-ft²- Degrees F |
AA; Typical at
77 Degrees F |
|
Melting Point |
502 - 638 Degrees C |
935 - 1180 Degrees F |
AA; Typical
range based on typical composition for wrought products 1/4 inch thickness
or greater. Eutectic melting is not eliminated by homogenization. |
|
Solidus |
502 Degrees C |
935 Degrees F |
AA; Typical |
|
Liquidus |
638 Degrees C |
1180 Degrees F |
AA; Typical |
Processing Properties |
| |
|
Annealing Temperature |
413 Degrees C |
775 Degrees F |
|
|
Solution Temperature |
256 Degrees C |
493 Degrees F |
Temper: 2024-0, 2024-T351,
2024-T3511,
2024-T851, 2024-T8511
Specification: QQ-A-225/6, QQ-A-200/4, AMS 4330, AMS 4120
2024-T4 Cold Finish Bar
Per QQ-A-225/6, AMS-QQ-A-225/6, ASTM-B-211
2024-T351 Cold Finish
Bar Per QQ-A-225/6, AMS-QQ-A-225/6, ASTM-B-211, AMS 4120
2024-T851 Cold Finish
Bar Per QQ-A-225/6, AMS-QQ-A-225/6, ASTM-B-211, AMS 4339
2024-T3 Extruded Bar
Per QQ-A-200/3, AMS-QQ-A-225/3, ASTM-B-211, AMS 4152
2024-T3511 Extruded
Bar Per QQ-A-200/3, AMS-QQ-A-200/3, ASTM-B-211, AMS 4165
2024
Aluminum Tube
2024 aluminum tubing is heavily utilized in aircraft
applications due to good machining characteristics and higher strength than
either 2014 or 2017. Cold formability is considered fair, yet it is one of the
most popular alloys for high strength tubing requirements because of the
superior grain structure that can be obtained.
2024-T3 Aluminum Tube
Per WW-T-700/3
1" OD X 0.095" Wall x
12 FT Per WW-T700/3
Please